The main components: The paint is made of epoxy resin, glass phosphorus film, pigments, fillers, plasticizers as a group, curing agent for the other component and prepared into a separate coating.
Uses: Suitable for steel equipment surface, pipelines, storage tanks, cement surface to prevent chemical corrosion, especially for heavy corrosion environment, tough film, water resistance, acid, alkali, salt corrosion, with good resistance to salt spray and hot and humid properties.
Product data: color flash point 32 °C
Solid content 66%
The proportion of 1.2 ~ 1.4kg/L
Theoretical coating rate 7 ~ 9m2/kg (25 to 35 microns dry film basis)
The actual coating rate allows the appropriate loss factor. Construction data: Airless spraying Recommended nozzles No. l7-23 Nozzle gas pressure 170-220 kg/cm2 Brush or roller for traditional spray Application Mix ratio A: B = 22:3 or 22:4, 22:6 (weight ratio)
Diluent special diluent (not more than 5% of the total volume)
Applicable period After mixing, use within 24 hours at 23°C. After blending, it must be cooked for 30 minutes before use. Drying time is 23°C.
Supporting and surface treatment:
Surface treatment: Sand blasting surface to Sa2.5 or mechanical derusting surface to ST3. Surface roughness reaches 30 to 70 microns.
Former auxiliary paints: Epoxy glass phosphorus primer, epoxy zinc-rich primer, iron red epoxy primer, cloud iron epoxy antirust paint, cloud iron epoxy intermediate paint, Hongdan epoxy antirust paint Other paints.
Construction conditions: The temperature of the construction surface and the paint itself must not be lower than 5°C. The construction surface must be clean and dry, and the temperature should be higher than 3°C above the dew point to avoid condensation. Relative humidity should be between 40 and 65%. Ventilation must be done during construction and drying in a confined space.
Storage: Store in a cool, dry environment with a valid storage period of one year. Over the storage period, the inspection may be carried out according to the items specified in this standard. If the results meet the requirements, they can still be used.
Packing: H52-26 Part A, 22 liters in a 20-liter container;
H52-26 component B, 5 (10) liters container 3 kg (4 kg, 6 kg).
Safety measures: General measures regarding the application of this product are (a) Take appropriate precautions to avoid skin and eye contact with paint (eg gloves, eyepieces, masks, protective oil, etc.).
(b) Maintain good ventilation.
(c) If the skin is contaminated with paint, apply soap or a suitable industrial cleaner and rinse with plenty of water.
(d) Since these products contain flammable substances, they should be kept away from sources of ignition and fireworks are strictly prohibited.
(e) Observe the safety instructions shown in the paint.
Additional notes: The actual amount used can vary depending on the construction environment, the geometry of the objects being coated, and the weather conditions.
Uses: Suitable for steel equipment surface, pipelines, storage tanks, cement surface to prevent chemical corrosion, especially for heavy corrosion environment, tough film, water resistance, acid, alkali, salt corrosion, with good resistance to salt spray and hot and humid properties.
Product data: color flash point 32 °C
Solid content 66%
The proportion of 1.2 ~ 1.4kg/L
Theoretical coating rate 7 ~ 9m2/kg (25 to 35 microns dry film basis)
The actual coating rate allows the appropriate loss factor. Construction data: Airless spraying Recommended nozzles No. l7-23 Nozzle gas pressure 170-220 kg/cm2 Brush or roller for traditional spray Application Mix ratio A: B = 22:3 or 22:4, 22:6 (weight ratio)
Diluent special diluent (not more than 5% of the total volume)
Applicable period After mixing, use within 24 hours at 23°C. After blending, it must be cooked for 30 minutes before use. Drying time is 23°C.
Supporting and surface treatment:
Surface treatment: Sand blasting surface to Sa2.5 or mechanical derusting surface to ST3. Surface roughness reaches 30 to 70 microns.
Former auxiliary paints: Epoxy glass phosphorus primer, epoxy zinc-rich primer, iron red epoxy primer, cloud iron epoxy antirust paint, cloud iron epoxy intermediate paint, Hongdan epoxy antirust paint Other paints.
Construction conditions: The temperature of the construction surface and the paint itself must not be lower than 5°C. The construction surface must be clean and dry, and the temperature should be higher than 3°C above the dew point to avoid condensation. Relative humidity should be between 40 and 65%. Ventilation must be done during construction and drying in a confined space.
Storage: Store in a cool, dry environment with a valid storage period of one year. Over the storage period, the inspection may be carried out according to the items specified in this standard. If the results meet the requirements, they can still be used.
Packing: H52-26 Part A, 22 liters in a 20-liter container;
H52-26 component B, 5 (10) liters container 3 kg (4 kg, 6 kg).
Safety measures: General measures regarding the application of this product are (a) Take appropriate precautions to avoid skin and eye contact with paint (eg gloves, eyepieces, masks, protective oil, etc.).
(b) Maintain good ventilation.
(c) If the skin is contaminated with paint, apply soap or a suitable industrial cleaner and rinse with plenty of water.
(d) Since these products contain flammable substances, they should be kept away from sources of ignition and fireworks are strictly prohibited.
(e) Observe the safety instructions shown in the paint.
Additional notes: The actual amount used can vary depending on the construction environment, the geometry of the objects being coated, and the weather conditions.